Browns and Tans and Irons:

Buttermilk

Gerstly Borate 10.5%
Kaolin 6.8%
Dolomite 6.8%
Talc 13.5%
Whiting 9.0%
Flint 24.1%
Potash Feldspar 29.3%
Opax 8.0%

Buttermilk

Gerstley Borate 13.0
Dolomite 6.0
Whiting 9.0
G200 spar 29.0 (or Custer)
EPK 6.0 (or whatever kaolin you are using)
Talc 16.0
Silica 21.0
Opax 8
Total 108.0

Carleton's Cream Glaze: This glaze does not combine well with oxides

Dolomite 33.33%
Feldspar 33.33%
Ball Clay 33.34%
  100 %

Paprika Spodumene

Custer 27%
Spodumene 18%
E.P.K. 25%
Dolomite 20%
Whiting 5%
F-4 Feldspar 5%
Tin 4.5%

Butter

Flint 23%
Custer 32%
Whiting 7%
E.P.K. 4%
Gerstly Borate 11%
Zinc oxide 5%
Zircopax 13%
Talc 5%
Rutile 5%
A wee little Albany mixed with water and you should get a nice soft pastel purple.  

This glaze is khaki brown where it is thin, and a deep brown-black where it is thick. Sometimes it has iron crystals in it that glisten.

K.C.N.S.T. OPAQUE SATIN IRON GLAZE: Khaki brown Cone 8-10

Feldspar 1839
Whiting 225
Kaolin 147
Flint 744
Red Iron Oxide 300

BRIGHT BROWN-BLACK SHINY OPAQUE CONE 10

Feldspar 1647 gr.
Whiting 620 gr.
Zinc Oxide 81 gr.
Kaolin 480 gr.
Flint 828 gr.
Red Iron Oxide 356 gr.

Cinnamon Ash:

Volcanic Ash 100 %
Ultrox 13 %
Bentonite 1 %

 

How about a Tan one?

Mixed Wood Ash 25%
Custer Spar 32%
Dolomite 12%
EPK 10%
Flint 18%
Magnesium Carbonate 2%
Also Add: 0
Red Iron Oxide 2%
Rutile 3%
CMC 1 tsp.

Tessha Rust cone 10

Potash Spar 22
Flint 25
Ball clay (om4) 24
Whiting 18
Red Iron Oxide 11

Michael Simon (Cone 8-10 Reduction)  (Can be applied to leather hard pots for once firing.)

Tessha Glaze

Whiting 18.52
Potash Feldspar 25.72
Ball Clay 27.88
Flint 27.88
Total 100.00%
ADD:  
Red Iron Oxide 11.32%

Unknown named glaze

Gerstly Borate 54.88%
Talc 14.63%
Flint 30.49%
Add: 100%
Red Iron Oxide 21.95%

Iron Red Plum

Cornwall Stone 442
Dolomite 45
Zinc Oxide 10
Whiting 112
E.P.K. 136
Flint 275
  1000
Red Iron Oxide 11.5%
Bentonite 2%

Wiser's Honey Cone 9-11

Potash Feldspar 36.7
Flint 25.5
Whiting 18.9
Ball Clay 9.2
Soda Feldspar 5.1
Kaolin 2.6
Dolomite 2.0
Red Iron Oxide 8.0%

Iron Glaze Cone 10

Bone ash 9
EPK 22
G200 47 (the original uses Custer Spar)
Talc 3
Whiting 19
Add  
RIO 4

Cone 10. Great over iron, copper and rutile.

Amblygonite 90%
Custer 10%

Dark Iron Glaze

Silica 27.7%
EPK 18.18%
Nepheline Syenite 18.18%
Dolomite 9.09%
Gerstly Borate 9.09%
Talc 9.09%
Bone Ash 9.09%
Iron 9.09%

Iron Rust Cone 9-10

Potash Feldspar 45%
Whiting 17%
Kaolin 13%
Silica 23%
Red Iron Oxide 13%

KAREN'S TOUCH GLAZE C/10 OX or RED

Kona F-4 feldspar 45
Dolomite 18
Whiting 4
EPK 9
Calcined kaolin 10
Tin oxide 4
Flint 10
Total 100%
Red iron oxide 1
Bone ash 4

Barnacle Bill Mars Matte

Cone: 9 - 10 Richard Burkett. Recipe: Percent Batch

Custer Feldspar 58.73 293.6
Dolomite 15.42 77.1
EPK 9.69 48.5
Talc 0.76 3.8
Flint 15.40 77.0
Totals: 100.00 % 500.0 gm
Also add: 0 0
Red Iron Oxide 16.51 82.6
Rutile 0.75 3.8
Manganese Dioxide 1.02 5.1

NOT a good candidate for a glaze for functional ware.

Unity Formula for Barnacle Bill Mars Matte:

0.235 K2O 0.504 Al2O3 3.787 SiO2
0.108 Na2O 0.004 Fe2O3 7.5:1 Si:Al Ratio
0.340 CaO
0.317 MgO

Percentage Analysis for Barnacle Bill Mars Matte:

66.85 % SiO2
15.11 % Al2O3
6.50 % K2O
1.97 % Na2O
5.62 % CaO
3.76 % MgO
0.18 % Fe2O3

 

KAKI GLAZES

Ohata Kaki Cone: 10

Recipe: Percent Batch
Potash feldspar 43.90% 7020
Silica 19.51% 3120
Kaolin 5.69% 910
Talc 5.69% 910
Whiting 6.50% 1039
Bone Ash 8.94% 1430
Red Iron Oxide 9.76% 1561
Totals: 100.00 % 15990 Gm

Unity Formula for Ohata Kaki:

0.177 K2O 0.357 Al2O3 3.508 SiO2
0.079 Na2O 0.218 Fe2O3 9.8:1 Si:Al Ratio
0.575 CaO 0.109 P2O5
0.169 MgO

Percentage Analysis:

58.86 % SiO2
10.17 % Al2O3
4.67 % K2O
1.37 % Na2O
9.00 % CaO
1.90 % MgO
9.72 % Fe2O3
4.30 % P2O5

Herbert Sanders Kaki

Nepheline Syenite 38.7%
Colemanite 20.0%
Zinc Oxide 8.10%
Barium Carbonate 9.85%
Kaolin 25.8%
Flint 33.0%
Red Iron Oxide 2 to 6 %

Kaki Glaze

Whiting 20%
Feldspar 30%
Kaolin 20%
Flint 30%
RIO 9%

Green:

Matte Green

Barium Carbonate 33.7%
Colemanite 27.37%
Dolomite 22.72%
Talc 5.6%
Spodumene 10.61%
  100%
Tin .86%
Chrome 2.60%
Rutile 1.37%

Green Matt

Barium 33.70%
Colemanite 27.37%
Dolomite 22.72%
Talc 5.6%
Spod 10.61%
Tin ox. .86%
Chrome 2.60%
Light Rutile 1.37%

Shaner Green

Kona A-3 45.0%
Talc 3.6%
E.P.K. 21.16%
Bone Ash 3.45%
Whiting 18.40%
R.I.O. 3.6%
Bentonite 1.84%

Blue green Satin Mat Clemson U 9/10

G-200 38.5%
Whiting 20%
EPK 20%
Flint 15%
Light Rutile 6%
Cobalt Carbonate 1%

Amy's Gray Glaze

Barium Carb 10.43%
Dolomite 15.57%
Cornwall 39.59%
Kaolin 21.47%
Flint 12.67%
  100.00%
Tin Oxide 3.26%
Black Nickel Oxide 1.00%

Rock Green cone 8-10

Potash Feldspar 40%
Whiting 30%
EPK 15%
Flint 30%
Zinc 5%
Iron 3%

Yellows:

Sunshine Yellow

Nepheline Syenite 60%
Barium Carb 25%
Dolomite 12%
Tin 3%
Superpax 10%
  100%
Red Iron Ox. 3%
Bentonite 2%

KT Yellow Cone 10Red

Nepheline Syenite 20.0%
Whiting 15.0%
Barium Carbonate 25.0%
Lithium Carbonate 3.0%
Ball Clay 25.0%
Flint 10.0%
Iron 2.0%

Shanner Gold

Bone ash 2.88%
Talc 3.8%
Whiting 20.1%
Potash 49.7%
Kaolin 23.6%
Yellow iron 3.8%
Rutile 3.88%

Oatmeal:

Feldspar 47
Gerstly Borate 4
Kaolin 15.4
Whiting 15
Flint 14
Ilmenite 2%
Rutile 2.3%

Pumpkin Fergerson

Potash Feldspar 9600 gr.
Kaolin 4608 gr.
Dolomite 3072 gr.
Whiting 1920 gr.
Tin 960 gr.
Bone ash 1536 gr.
Rutile 1084 gr.
Iron 217 gr.

Gilstrap Yellow

Potash Feldspar 76%
Whiting 42%
Kaolin 40.4%
Flint 30.4%
Rutile 97%
Red Iron 13.6%

Tenmoku Glazes/Temmoku Glazes

We tried to call this up on spell check and all it said was "Black breaks Brown"!

Black Tenmoku. Cone 9-10

Potash Feldspar 52%
Whiting 14%
Kaolin 6%
Silica 19%
Red Iron Oxide 9%

Oil Spot Temmoku

Albany 2796 gr.
Potash 2232 gr.
Kentucky 558 gr.
Red Iron 282 gr.
Borax 238 gr.

Temmoku: Base glaze for R Chun

Raval Feldspar 65.00%
Whiting 18.00
Rice straw ash 7.00
Silica 10.00
Add: 0
Iron Ox. 6.50

Any high silica ash would be a good substitute, grass ash should work well, rice straw is about 98% silica with high phosphorous content.

Tenmoku glaze

Feldspar 1700
Whiting 300
China clay 200
Silica 400
Iron 200